The rotating cylinder electrode (RCE) is a technique used in corrosion research to simulate in a laboratory environment the turbulent flow, which usually occurs when liquids are transported through pipelines.

The corrosion of the inner walls of pipelines occurs due to the electrochemical interaction between the pipe material and the fluids that flow through the pipes. The corrosion of pipes is significantly enhanced by the turbulent nature of the flow, occurring inside the pipelines.

The rotating cylinder electrode (RCE) is used to generate a turbulent flow at the surface of a sample, in a laboratory environment, simulating the pipe flow conditions. In other words, the turbulent flow of a liquid with known flow rate through a pipeline of given internal diameter and its effect on the material surface can be reproduced in a laboratory environment by using and RCE with a given cylinder size (made of the same material as the pipe) which spins at a well-defined rotation rate.

Therefore, one of the main applications of RCE is to test the efficiency of corrosion inhibitors and the corrosion susceptibility of pipe materials in simple and fast electrochemical experiments, simulating the pipe flow conditions.

Experiments that involve an RCE are regulated by the ASTM G185 standard [1].

In this application note, The RCE with a 1018 carbon steel cylinder sample was used with the linear polarization (LP) measurement technique. Two LP experiments were conducted, one without a corrosion inhibitor and the other with a corrosion inhibitor added to the electrolyte.

The corrosion potential E_corr (V) was measured, as being E_corr = −0.479 V in the case of the electrolyte without inhibitor, and E_corr = −0.392 V in the case of the electrolyte with the inhibitor.

In Figure 2, the voltammograms resulting from the Linear Polarization (LP) experiments are shown. In blue, the data measured without inhibitor, and in red the data measured with the inhibitor added to the electrolyte are presented.

Figure 2 shows that the data with the inhibitor appears on the right side of the plot, with respect to the data without inhibitor. This means that in the case of the electrolyte with the inhibitor, the same current values occur at potential higher (more noble) than the electrolyte without the inhibitor.

In LP measurements, the inverse of the slope of the i vs. E plot near E_corr can be used to estimate the polarization resistance values (R_p , Ω).

When the inhibitor is added to the system, a decrease in the slope is observed, indicating that R_p has increased.

A linear regression around E_corr (not shown here) helped to calculate R_p. In the case of the LP measurements without inhibitor, a value of R_p = 42.62 𝛺 is found. In the presence of the inhibitor, the value of R_p = 135.96 𝛺 is found.

In Figure 3, the Tafel plots are shown.

There, the E_corr can be easily determined, being the potential value where the current drops to zero, the position of the negative spike in the log(i) vs E plot.

The data analysis is further performed and additional corrosion parameters can be calculated by using the Corrosion rate analysis command in the NOVA software.

The calculated polarization resistance for the sample in the electrolyte without inhibitor was R_p = 43.32 𝛺 and for the sample in the electrolyte with the inhibitor R_p = 136.39 𝛺. The results were similar with those discussed before which were obtained with the linear regression of LP measurements. Table 1 compares the results obtained from the linear regression and the corrosion rate analysis, with and without the inhibitor. The values of the corrosion rates are also listed.

The fact that the value of the R_p calculated with the corrosion rate analysis is close to the value calculated with the linear regression of the LP is an additional indication that the calculated corrosion parameters are valid. It can be seen that the corrosion rate of the material in the solution with the inhibitor (0.065 mm year ⁻¹) is much lower than the corrosion rate measured in the same conditions in the electrolyte without the inhibitor (0.25 mm year ⁻¹).

According to the ASTM standard G185, the inhibitor efficiency can be calculated with the following Equation:

Where CR_no inhib  (mm year⁻¹) is the corrosion rate calculated without inhibitor, and CR_inhib (mm year⁻¹) is the corrosion rate calculated in the presence of the inhibitor.

Using the corrosion rate from the corrosion rate analysis (Table 1), the inhibitor efficiency is calculated at 74%.

This application note exemplifies a common use of the rotating cylinder electrode in the field of industrial and academic corrosion research. Two electrolytes were employed, one of them containing a tryptamine-based corrosion inhibitor. Linear polarization experiments were performed at 500 RPM rotation rate, corresponding to a fluid velocity 𝑣_RCE = 82.3 cm s⁻¹ (2.7 ft s⁻¹) inside a pipe with schedule 40, with an internal diameter of 30.32 cm (12′′). The effect of the inhibitor was evaluated from visual observation, linear regression, and corrosion rate analysis of linear polarization data.

Finally, the inhibitor efficiency was calculated, showing that the corrosion rate in the presence of the inhibitor is 74% lower than without the inhibitor.